性能(properties) 330# 310# 304# 446# 430#
熔點範圍，℃ Melting point℃ 1400~1425 1400~1450 1400~1450 1425~1510 1425~1510
876度時的彈性模量104Mpa。
Spring module at 876℃ 104Mpa 13.4 12.4 12.4 9.65 8.27
870度時的抗拉強度Mpa
Tensile strength at 870℃, Mpa 193 152 124 52.7 129
870度時的熱膨脹係數10~6/度
Heat-shrinking coefficient at 870℃, 10~6/10~6/℃ 17.64 18.58 20.16 13.14 13.68
500度時的熱傳導，W/m.k
Heat-conductibility at 500℃ W/m.k 21.6 18.7 21.5 24.4 26.3
室溫下的比重，g/cm3
Proportion at room temp., g/cm3 8.0 8.0 8.0 7.5 7.8
982度迴圈氧化1000小時後的重量損失，%
Weight loss after circular oxidation about 1000 hours at 982℃,% 18 13 70 4 70
H2S中的腐蝕率
Erosion in the H2S,mil/yr / 100 200 100 200
SO2中推薦的 使用溫度，度
2 ,℃ / 1050 800 1025 800
815度天然氣中的腐蝕率，mil/yr
Erosion in the natural gas at 815℃,mil/yr  3  4 12
982度，焦爐 中的腐蝕率，mil/yr
Erosion in the coal gas from the cookery at 982℃,mil/yr 75 25 225 14 236
525度無水氨中的氮化率，mil/yr
Nitrification in the anhydrous ammonia at 525℃,mil/yr 20 55 80 175 80~175
454度 H2腐蝕率，mil/yr
Erosion in the H2,at 454℃,mil/yr   2.3 4.8 8.7 21.9
982度,25小時，4次迴圈，
固體氮化後，合金增碳量，%
Carbon content of the alloy after solid carbonizing about 25 hours at 982℃,% 0.08 0.02 1.40 0.07 1.03

石化爐窯石化爐窯耐熱不鏽鋼纖維應用領域：
冶金工業：加熱爐的爐頂、爐頸、爐門、燒嘴磚、水冷管包紮、出鋼槽槽底、步進爐爐底、環形爐擋火牆、均熱爐爐蓋、凸出帶、砂封口、中間包包蓋、電爐三角區、鐵水包襯裏、爐外精煉用噴 、底吹氧煙道、鐵水溝蓋、擋渣堰、高爐中各種耐火料襯裏，煉焦爐門裏等。
水泥工業：迴轉窗的鏈條帶、加熱帶、加熱器蓋、空氣進口和燃燒管，其他窯的易磨和易衝擊部位。
石油化工業：鋼纖維用於石化裝置中的滑動閥門，裂口區壓力吹風管，以增加抗熱震，抗磨能力和降 。
傳送線、提升器和旋風器襯裏，用鋼纖維增強後，可防止其分層啓縐、磨損和開裂、燒嘴磚、爐頂、傳送部分和加熱器粗嘴，採用鋼纖維澆注後，消除和減少了裂紋和剝落。
石油催化裂化裝置旁路煙道，採用鋼纖維澆注料後解決了熱震和熱迴圈問題。
鋼纖維在石油方面的 應用是將它與澆注料一起噴射在襯裏的錨固系統上，鋼纖維的錨固件一起進行增強，愈與龜甲鋼襯裏比較不僅使總施工費減少了50%，而且增加了抗機械應力和熱應力，經濟效益十分明顯。